flux core/argon gas .035-.045

can spray transfer be used on mild steel 1/8"-1/4" and how to determine distortion while spray arc?


yes spray arc can be used and will distort more than short circuit transfer mig.

travel speeds will be faster but welds will be much hotter and like i said, will distort more.

Comments for flux core/argon gas .035-.045

Average Rating starstarstarstarstar

Click here to add your own comments

Nov 28, 2010
flux core/argon gas .035-.045
by: Anonymous

since spray arc will distort weldment even with a fast rate would the globular method be best to minimize heat distortion, undercut, or other weld defects with flux-core?

Click here to add your own comments

Return to mig fcaw forum.

Enjoy this page? Please pay it forward. Here's how...

Would you prefer to share this page with others by linking to it?

  1. Click on the HTML link code below.
  2. Copy and paste it, adding a note of your own, into your blog, a Web page, forums, a blog comment, your Facebook account, or anywhere that someone would find this page valuable.