TIG ALUMINUM 11GA BUTT 1G
scroll down for settings used
You might like these
A good Test for any Tig Welding Machine arc starts is welding Coke Cans
Welding anodized aluminum is what everyone wants to learn
The best Aluminum Welding Training you can get on your own - How to Get better at Tig Welding
WELD PROCESS = TIG, GTAW, GAS TUNGSTEN ARC WELDING
METAL TYPE = ALUMINUM 6061
THICKNESS = 1/8"
WELD TYPE = GROOVE WELD
JOINT TYPE = BUTT
POSITION = 1G
AMPERAGE = 140 CONTROLLED WITH FOOT PEDAL
TUNGSTEN = 2% LANTHANATED, 3/32"
FILLER WIRE = 3/32” 4943
POLARITY = AC
GAS FLOW = 15 CFH argon
CUP SIZE = 6
ADDITIONAL SETTINGS = AC BALANCE 30% CLEANING, AC FREQ 100HZ
PRE FLOW = 1 SEC
POST FLOW = 10 SEC
TIPS: KEEP A FAIRLY TIGHT ARC AND WATCH TORCH ANGLE
Aim for an arc length that is equal or less than the diameter of your tungsten electrode.Torch angle can be forgiving provided your arc length is tight.
Did you know?...
*** We have a New TIG course learning system over at welderskills.com designed to help you learn faster, with less frustration, and with less metal.
***And that you will get Free Access to this $99.99 TIG course... included as part of your membership?
***And that you can watch as much as you like during your free week trial?
***And that if you use promo code LPZ1 you can get 50% off your first month after your Free 7 day Trial?
***Its Easy to sign up
Even easier to cancel ...no hoops to jump thru.
No Ads, No BS style
Invest in yourself and sign up for the free test drive today.
You might like these
A good Test for any Tig Welding Machine arc starts is welding Coke Cans
Welding anodized aluminum is what everyone wants to learn
The best Aluminum Welding Training you can get on your own - How to Get better at Tig Welding
Enjoy this page? Please pay it forward. Here's how...
Would you prefer to share this page with others by linking to it?
- Click on the HTML link code below.
- Copy and paste it, adding a note of your own, into your blog, a Web page, forums, a blog comment,
your Facebook account, or anywhere that someone would find this page valuable.